Research article

|

|

The effect of various modifications/intercalations of halloysite and the combination of these modifications with in situ PP matrix modification was investigated with respect to the structure and properties of the polypropylene/halloysite nanocomposites. Hexadecyl-tri-methyl-ammonium-bromide (HEDA), 3-aminopropyltrimethoxysilane and urea were used as the intercalators/modifiers. The best intercalation was found for urea, although an unexpected insignificant impact on the mechanical properties also resulted as a consequence of the urea polarity and the significant decrease in PP crystallinity. However, the simultaneous application of 4,4!-diphenylmethylene dimaleinimide (DBMI) brought about an increase in the mechanical behavior by increasing the halloysite/PP affinity as a result of in situ matrix modification. This effect was further supported by coupling between the PP and halloysite (HNT) in the system containing urea-intercalated HNT. This can be explained by the occurrence of a urea-supported reaction between the imide ring of DBMI and the OH groups of the HNT, which resulted in the best mechanical behaviors achieved in this study.